Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Nature Communications volume 14, Article number: 5640 (2023 ) Cite this article Fertilizer Water
Electrochemical CO2 reduction in acidic electrolytes is a promising strategy to achieve high utilization efficiency of CO2. Although alkali cations in acidic electrolytes play a vital role in suppressing hydrogen evolution and promoting CO2 reduction, they also cause precipitation of bicarbonate on the gas diffusion electrode (GDE), flooding of electrolyte through the GDE, and drift of the electrolyte pH. In this work, we realize the electroreduction of CO2 in a metal cation-free acidic electrolyte by covering the catalyst with cross-linked poly-diallyldimethylammonium chloride. This polyelectrolyte provides a high density of cationic sites immobilized on the surface of the catalyst, which suppresses the mass transport of H+ and modulates the interfacial field strength. By adopting this strategy, the Faradaic efficiency (FE) of CO reaches 95 ± 3% with the Ag catalyst and the FE of formic acid reaches 76 ± 3% with the In catalyst in a 1.0 pH electrolyte in a flow cell. More importantly, with the metal cation-free acidic electrolyte the amount of electrolyte flooding through the GDE is decreased to 2.5 ± 0.6% of that with alkali cation-containing acidic electrolyte, and the FE of CO maintains above 80% over 36 h of operation at −200 mA·cm−2.
Electrochemical reduction of CO2 at ambient temperature is a promising technique to store renewable electricity, fix CO2 and produce valuable fuels and chemicals1,2. One of the greatest challenges to make this technique industrially feasible is to prevent the formation of (bi)carbonate at the cathode3,4. Alkaline solution is not a practical electrolyte for CO2 reduction due to the reaction between OH- and CO25,6. When carrying out CO2 reduction in near neutral electrolyte such as KHCO3 solution, partial CO2 is consumed by OH- ions generated on the cathode to form HCO3- or CO32- instead of being reduced. The as-formed HCO3- or CO32- ions migrate to the anode and are acidified by H+ generated on the anode, which gives rise to CO2 crossover from cathode to anode3,7,8. This process results in low utilization efficiency of CO2. Moreover, the high resistance of the near neutral electrolyte leads to low energy efficiency at high current density9.
Recently, techniques of CO2 reduction with acidic electrolyte were developed to circumvent the as-mentioned issues9,10,11,12,13,14,15,16,17,18,19,20,21. Alkali cations play an important role to suppress hydrogen evolution reaction (HER) and promote CO2 reduction in acidic condition. However, alkali cations induce bicarbonate precipitation on the cathode during CO2 reduction in acidic electrolyte, which is still an issue that hinders the sustainability of CO2 reduction22,23. Fig. 1a illustrates the formation process of bicarbonate precipitate on the cathode. In spite of the low pH of bulk electrolyte, CO2 is able to convert to HCO3- in the vicinity of the cathode with high local pH12,13,24. The as-formed HCO3- is then combined with the high concentration of alkali cations accumulated at the local environment of the cathode, causing the precipitation of alkali metal bicarbonate. The bicarbonate precipitate can destroy the hydrophobicity of the gas diffusion electrode (GDE) and thus induce flooding, which can block the channel for the mass transport of CO25,23,25,26,27. The inset of Fig. 1a shows the energy dispersive spectroscopy (EDS) mapping of the cross-section of Ag/GDE after CO2 reduction with H2SO4-K2SO4 electrolyte, which explicitly shows the permeating of K+-containing electrolyte through the GDE. Besides, when alkali cation-containing acidic electrolyte is used in a two-chamber cell with proton exchange membrane (PEM), the pH values of catholyte and anolyte change in the long-term electrolysis. As illustrated in Fig. 1b, the mole H+ consumed on the cathode equals that generated on the anode. However, both H+ and alkali cations can traverse most PEMs, while the alkali cations cannot be consumed on the cathode. As a result, alkali cations accumulate in the catholyte and H+ ions accumulate in the anolyte, leading to the increase of pH of the catholyte and the decrease of pH of the anolyte. Therefore, a possible strategy to maintain the hydrophobicity of the GDE and the composition of the electrolyte during CO2 reduction is to use metal cation-free acidic electrolyte.
a Proposed mechanism of the formation of KHCO3 precipitate on GDE with K+-containing acidic electrolyte. The inset shows the EDS mapping of the cross-section of Ag/GDE after CO2 electroreduction experiment in 0.1 M H2SO4 + 0.4 M K2SO4. Green and yellow regions represent the distribution of K and Ag elements, respectively. b Migration of cations in the two-chamber cell with PEM. tH+ and tK+ represent the transference number of H+ and K+ in the PEM, respectively. c Effects of K+ ions on the adsorption of *CO2 intermediate and the migration of H+. The dashed black line indicates the OHP. The green curve illustrates the concentration profile of K+. d Effects of immobilized layer of cations on the adsorption of *CO2 intermediate and the migration of H+. μ and E in c, d represent the dipole moment of adsorbed *CO2 intermediate and the electric field in Stern layer, respectively.
Different mechanisms of cation effect in acidic electrolyte have been proposed. Hydrated cations at the outer Helmholtz plane (OHP) show distinct acidity compared with those in bulk solution, which is considered to tune the reactivity of HER and CO2 reduction near the cathode28,29. More importantly, cations accumulate near the OHP modulate the distribution of electric field in the electric double layer. On one hand, cations screen the electric field generated from the cathode and thus retard the migration of H+9,22. On the other hand, cations enhance the electric field in Stern layer, which stabilizes the adsorbed polar intermediates of CO2 reduction such as *CO2 (Fig. 1c) and *OCCO30,31,32. Owing to these effects, H+ reduction is suppressed and CO2 reduction is promoted. Moreover, it was reported that partially dehydrated alkali cations at the OHP can further stabilize the adsorbed polar intermediates via a short-range electrostatic interaction29,33. This effect was considered indispensable for enabling CO2 adsorption and C-C coupling for the formation of C2+ products29,33. All the as-mentioned effects arise from cations accumulating near the cathode rather than those in the bulk electrolyte. Therefore, a layer of cations immobilized on the surface of the cathode may also enable CO2 reduction in acidic condition without metal cations dissolved in the bulk electrolyte (Fig. 1d). Cationic polyelectrolytes are promising candidates for this task.
In this work, cross-linked poly-diallyldimethylammonium chloride (denoted as c-PDDA) was used as an immobilized cationic layer to cover the catalysts for CO2 reduction. Aqueous solution of H2SO4 was used as the electrolyte. CO and formic acid were selectively generated with silver (Ag) and indium (In) nanoparticles (NPs) as the catalysts, respectively. The performance was stable over 36 hours and the pH values of both catholyte and anolyte kept constant. In sharp contrast, when K+-containing acidic electrolyte was used, the pH value of catholyte increased by 5.3 unit after electrolysis for 10 hours. Moreover, with metal cation-free acidic electrolyte, the amount of electrolyte flooding through the GDE was 1% of that with K+-containing acidic electrolyte, indicating that the hydrophobicity of the GDE was highly retained with metal cation-free electrolyte. This work provides the strategy to improve the sustainability of CO2 electroreduction in acidic condition.
In metal cation-containing acidic electrolyte, the electric field distribution is modulated by the accumulated cations in the electric double layer, which suppresses H+ reduction and promotes CO2 reduction9,22. Inspired by this mechanism, we designed to immobilize a layer of cationic polyelectrolyte on the cathode to enable CO2 reduction in metal cation-free acidic electrolyte. As shown in Fig. 2a, Ag NPs (99.99%, <100 nm, Macklin) showed negligible Faradaic efficiency (FE) of CO in a flow cell with 0.1 M H2SO4 as the electrolyte (black line). When Sustainion XA-9, a commercial cationic polyelectrolyte34, was added with the catalyst, around 1% FE of CO was detected (orange line). The low FE of CO can be ascribed to the fact that the cation density of Sustainion XA-9 (2.06 mmol g-1)34 is not high enough to substantially affect the electric field distribution. Poly diallyldimethylammonium chloride (PDDA) possesses the cation density of 6.19 mmol·g-1, 3 times that of Sustainion XA-9, which is the highest cation density we can find in a wide variety of polyelectrolytes. However, the PDDA decorated Ag NPs shows unsatisfactory CO2 reduction performance. The FE of CO was measured to be slightly higher than 2% at 15 min of electrolysis and dropped to below 1% after 30 min (blue line). The low performance of PDDA decorated Ag NPs can be attributed to the high solubility of PDDA in water. During the electrolysis, PDDA was washed away from the catalyst by the flowing catholyte and could not form a stable layer to cover the catalyst. Figure S1a, b compares the X-ray photoelectron spectroscopy (XPS) of PDDA decorated Ag catalyst before and after electrolysis. The peak of N 1 s decreased substantially after electrolysis, indicating the loss of the layer of PDDA. 1H-NMR spectrum of the electrolyte after electrolysis (Figure S2) indicates that about 90% of PDDA was washed into the electrolyte.
a FE of CO during electrolysis with constant current density of −200 mA·cm-2. Bare Ag NPs (black), Sustainion XA-9 decorated Ag NPs (orange), PDDA decorated Ag NPs (blue) and c-PDDA decorated Ag NPs (magenta) with 0.1 M H2SO4 as the flowing electrolyte, together with bare Ag NPs with 0.1 M H2SO4 + 0.4 M K2SO4 as the flowing electrolyte (gray). The insets show the structures of PDDA (blue) and Sustainion XA-9 (orange). b Schematic of c-PDDA decorated catalyst. The blue lines represent the polymer chains, and the short red lines represent the -(CH2)6- cross-linkers. c The pH values of the catholyte and anolyte during electrolysis with constant current density of −200 mA·cm-2. 0.1 M H2SO4 or 0.1 M H2SO4 + 0.4 M K2SO4 were used as the flowing electrolyte. d Mass of electrolyte permeating through the cathode after electrolysis with constant current density of −200 mA·cm-2 for 10 h. Error bars are the standard deviations based on three individual measurements. Source data are provided as a Source Data file.
To prevent the layer of PDDA on the surface of catalyst from being washed away, we designed a cross-linked polyelectrolyte that can adhere firmly onto the catalyst, as illustrated in Fig. 2b. Figure S3 schematically shows the procedure of the preparation of c-PDDA decorated catalysts. First, we prepared the copolymer of diallyldimethylammonium chloride (DADMACl) and diallylmethylamine (DAMA). Figure S4 shows the characterizations of the copolymer. The N 1 s XPS spectrum (Figure S4b) shows two peaks at 399.0 eV and 402.0 eV with the area ratio of 1:3.8, corresponding to the tertiary amine sites35 and quaternary ammonium sites36,37, respectively. 1,6-diiodohexane was chosen as the cross-linking agent to link the tertiary amine sites in two copolymer chains. To prepare the working electrode, the catalyst, the copolymer, 1,6-diiodohexane, ethylene glycol and ethanol were mixed as the ink and dropped onto the GDE. The GDE was then heated to facilitate the cross-linking reaction and evaporate the solvent. Figure S5 shows the high angle annular dark field-scanning transmission electron microscopy (HAADF-STEM) and EDS mapping images of Ag NPs coated with c-PDDA, in which N element distributes uniformly over Ag NPs. The N 1 s XPS of this sample (Figure S1d) shows a single peak at 402.0 eV, indicating all the tertiary amine sites in the copolymer were converted to quaternary ammonium sites. The cation density of c-PDDA was measured to be 5.80 mmol g-1 and the charge density of c-PDDA immersed in water (denoted as ρp) was measured to be +296 C cm-3 (corresponding to 3.07 M of cationic sites). The procedure of the measurement is shown in the Methods section. As shown by the magenta line in Fig. 2a, c-PDDA decorated Ag NPs presented the FE of CO up to 90% and kept above 80% during electrolysis for 36 h at −200 mA·cm-2 in 0.1 M H2SO4. Figure S6 shows the electrode potential during the chronopotentiometry experiment. As presented in Figure S1c, d, the peak intensity of N 1 s in the XPS spectra did not change obviously after electrolysis, confirming the c-PDDA layer was retained on the surface of Ag NPs. Figure S7 and S8 shows the infrared (IR) spectra and the electrochemical impedance spectra (EIS) of the working electrode before and after electrolysis, respectively. No substantial change in the spectra was observed, indicating both the polymer layer and the interface between Ag NPs and the polymer were stable during electrolysis. Inductively coupled plasma-mass spectroscopy (ICP-MS) analysis of the electrolyte after electrolysis showed that the concentrations of Na+ and K+ were 6.0×10-6 M and 5.5×10-6 M, respectively. To rule out the possibility that it was this trace amount of alkali cations rather than c-PDDA enabled CO2 reduction in acidic electrolyte, 0.1 M of 18-crown-6 was added into 0.1 M H2SO4 to chelate alkali cations. The FEs of CO at −100 mA·cm-2 in 0.1 M H2SO4 with and without 0.1 M of 18-crown-6 were 93% and 95%, respectively. The addition of 18-crown-6 did not obviously affect the FE of CO, indicating that the trace amount of alkali cations is not the origin of CO2 reduction activity.
When K+-containing acidic solution (0.1 M H2SO4 + 0.4 M K2SO4) was used as the electrolyte, the FE of CO on bare Ag NPs also reached 90% initially. However, it dropped to below 80% after 2 hours and decreased to 43% after 10 hours (gray line in Fig. 2a). The poor stability of the electrocatalytic performance can be ascribed to the existence of K+ in the acidic electrolyte. As shown by the magenta and orange lines in Fig. 2c, when 0.1 M H2SO4 was used as the electrolyte, the pH values of both catholyte and anolyte kept around 1.0 in 10 h. Under this circumstance, H+ is the only kind of ion that can migrate through the PEM. When 0.1 M H2SO4 + 0.4 M K2SO4 was used as the electrolyte, the pH of catholyte increased and the pH of anolyte decreased over time. Specifically, the pH values of the catholyte and the anolyte changed from 1.6 to 6.9 and 0.8 after 10 h, respectively (black and gray lines in Fig. 2c). Since the migrations of both H+ and K+ contribute to the current across the PEM (Nafion 211), the migration rate of H+ through the PEM was lower than the generation rate of H+ at the anode or the consuming rate of H+ at the cathode (Fig. 1b). Consequently, the concentration of H+ decreased and the concentration of K+ increased in the catholyte. The pH of catholyte was convergent to about 7 because of the buffering effect of CO2. The existence of K+ in the electrolyte also led to the formation of KHCO3 precipitate on the GDE, as indicated by X-ray diffraction (XRD) and scanning electron microscopy (SEM) characterizations (Figure S9). The increase of the pH and the concentration of K+ in the catholyte facilitated the precipitation of KHCO3. As shown in Figure S10, the contact angle of water on the side of gas diffusion layer of the working electrode after electrolysis in 0.1 M H2SO4 + 0.4 M K2SO4 was considerably smaller than that after electrolysis in 0.1 M H2SO4, indicating that the formation of KHCO3 precipitate reduced the hydrophobicity of the GDE. The break-down of the hydrophobicity led to the electrolyte flooding and blocked the mass transport of CO2. To quantify the electrolyte flooding, we measured the mass of electrolyte permeated through the GDE during 10 h of electrolysis. When 0.1 M H2SO4 + 0.4 M K2SO4 was used as the electrolyte and bare Ag NPs were used as the catalyst, 43 ± 17 mg of the electrolyte permeated through 1 cm2 of GDE. When 0.1 M H2SO4 was used as the electrolyte and c-PDDA decorated Ag NPs were used as the catalyst, only 1.1 ± 0.4 mg of the electrolyte permeated through 1 cm2 of GDE (Fig. 2d). The procedure of the measurement is shown in the Method section. It is noteworthy that the increase of the pH of the catholyte did not directly cause the decrease of the FE of CO on bare Ag NPs. As shown in Figure S11, the initial FEs of CO on bare Ag NPs in electrolytes with varied pH are all around 90%. The decrease of the FE of CO in 0.1 M H2SO4 + 0.4 M K2SO4 in Fig. 2a was a direct consequence of the formation of KHCO3 precipitate.
Figure S12 further compares the FE of CO on bare Ag NPs in 0.1 M H2SO4 + x M K2SO4 (x = 0.04 ~ 0.4). As shown by our previous study22, by decreasing the concentration of K+, the stability was improved while the initial FE of CO decreased. 0.1 M H2SO4 + 0.1 M K2SO4 was an optimized composition of electrolyte that balance the FE of CO and stability22. In this electrolyte, the FE of CO was around 80% initially, lower than that in 0.1 M H2SO4 + 0.4 M K2SO4, while the decrease of FE of CO was slower. After 3 hours, the FE of CO became higher than that in 0.1 M H2SO4 + 0.4 M K2SO4 but significantly lower than that of c-PDDA decorated Ag NPs in 0.1 M H2SO4. The CO2 reduction performance of c-PDDA decorated Ag NPs in 0.1 M H2SO4 + 0.4 M K2SO4 was also measured, as shown in Figure S12. The FE of CO was higher than bare Ag NPs in 0.1 M H2SO4 + 0.4 M K2SO4 in 10 hours, suggesting that the formation rate of KHCO3 precipitate decreased. However, the performance of c-PDDA decorated Ag NPs in 0.1 M H2SO4 + 0.4 M K2SO4 was less stable than in 0.1 M H2SO4, and KHCO3 precipitate was still detectable after CO2 reduction for 12 h (Figure S13), indicating that the c-PDDA layer can slow down but not prevent the formation of KHCO3 precipitate.
Figure 3 shows the FEs of different products from CO2 reduction in 0.1 M H2SO4 with c-PDDA decorated Ag NPs and In NPs as the catalysts. Figure S14 shows the TEM images and the XRD pattern of In NPs. CO and formic acid were selectively produced on Ag NPs and In NPs, respectively. For Ag NPs, the highest FE of CO was 95 ± 3%, achieved at −1.57 ± 0.04 V vs standard hydrogen electrode (SHE) at the current density of −100 mA·cm-2. At the current density of 300 −mA·cm-2, the FE of CO was 82 ± 4%, corresponding to a partial current density of CO of −246 ± 12 mA·cm-2. When 1 M H2SO4 was used as the electrolyte, the highest FE of CO was 66%, achieved at the current density of −300 mA·cm-2, corresponding to a partial current density of CO of −198 mA·cm-2 (Figure S15). For In NPs, the highest FE of formic acid reached 76 ± 3%, at −1.84 ± 0.08 V vs SHE with the current density of −200 mA·cm-2. At the current density of −300 mA·cm-2, the FE of formic acid was 75 ± 4%, corresponding to a partial current density of formic acid of −225 ± 13 mA·cm-2. In the electrolyte after CO2 reduction experiments, Ag and In elements were not detectable by ICP-MS, indicating less than 0.2% of Ag or In was dissolved during electrolysis. Although the standard reduction potential (φ°(In3+/In) = −0.34 V vs SHE)38 indicates metallic In can be oxidized by H+ in a chemical reaction, In catalyst was stable in 0.1 M H2SO4 at the electrode potential for CO2 reduction (<−1.3 V vs SHE). As shown in Figure S16, the selectivity of CO2 reduction conducted on c-PDDA decorated catalysts in 0.1 M H2SO4 is higher than that on bare catalysts in 0.1 M H2SO4 + 0.1 M H2SO4 or 0.1 M H2SO4 + 0.04 M H2SO4 at varied current density. When undecorated Ag NPs and In NPs were used as the catalysts in 0.1 M H2SO4, H2 was only reduction product (Figure S17). Figure S18 further compares the overall cell potential and each component of the potential loss at different current densities with 0.1 M H2SO4, 0.1 M KHCO3 and 0.1 M KOH as the electrolyte. The potential loss is composed of ohmic loss, overpotentials of cathodic reaction and anodic reaction. The cell potential with 0.1 M H2SO4 is the lowest due to the lowest resistance of the electrolyte. The apparent overpotential of CO2 reduction in 0.1 M KOH is the lowest9,25, but KOH solution is not sustainable during electrolysis and is not a practical choice as the electrolyte for CO2 reduction techniques. The cell potential with 0.1 M KHCO3 is the largest due to the highest resistance of the electrolyte.
a Ag NPs and b In NPs were used as the catalysts. Chronopotentiometry experiments were conducted. The FEs of H2 (gray), CO (orange) and formic acid (blue), and the electrode potential (dark blue curves) are shown. Error bars are the standard deviations based on three individual measurements. Source data are provided as a Source Data file.
It was reported that immobilized quaternary ammonium cations on ionomer can enable CO2 reduction on membrane electrode assembly (MEA) with pure water as the anolyte39,40, implying that the quaternary ammonium cations have the ability to interact with *CO2 species and promote CO2 reduction in alkali cation-free condition. The interaction between quaternary ammonium cation and the adsorbed species weakens as the substituent groups on the N atom become bulkier41. The N atoms in PDDA bears two methyl groups, the smallest substituent group. Therefore, PDDA should show stronger interaction with *CO2 species than quaternary ammonium cations with other substituent groups. In the alkali cation-containing electrolyte, the partially dehydrated alkali cation at OHP can bind to *CO2 species, which is essential for triggering CO2 reduction29,33. Since the quaternary ammonium cation cannot directly bind to *CO2, the short-range interaction between *CO2 and the quaternary ammonium cation should be weaker than that between *CO2 and alkali cations. In addition, both alkali cations and quaternary ammonium cations can increase the electric field strength in Stern layer, which also stabilizes the polar *CO2 intermediate, as discussed in the following section. Taking all the effects into account, K+ should show more profound promotion effect on the kinetics of CO2 reduction than c-PDDA, in accordance with our observation that the applied potential to reach the same partial current density of CO on bare Ag NPs in K+-containing electrolyte (with K+ concentration of 0.08 ~ 0.8 M) was more positive than on c-PDDA decorated Ag NPs in K+-free electrolyte (Figure S19).
Our previous works indicate that alkali cations enable CO2 reduction in acidic electrolyte through retarding the migration of H+ and enhancing the electric field in Stern layer9,22. In this work, we used a layer of c-PDDA immobilized on the catalyst to take over the role of alkali cations in electrolyte. The effect of the cationic polyelectrolyte adlayers on CO2 reduction in alkali cation-containing neutral electrolyte has been studied. In neutral electrolyte, the polyelectrolyte can modulate the concentration distribution of HCO3-, CO32- and OH- through Donnan exclusion and thus tune the local pH41,42. It was also reported that the polyelectrolyte layer can affect the local water content and CO2 concentration24,42. In acidic electrolyte, the concentration distribution of H+ can also be tuned by the polyelectrolyte through Donnan exclusion. More importantly, the polyelectrolyte layer may affect the rate of H+ mass transport and hence determine the rate of H2 evolution from H+ reduction. The polyelectrolyte may also modulate the electric field in Stern layer and determines the rate of the electron transfer from cathode to CO2. To understand these effects, we conducted experiments with Ag micro-disk electrode (MDE) covered by different polymers and simulated the experiments with generalized modified Poisson-Nernst-Planck (GMPNP) modeling43,44.
The black curve in Fig. 4a shows the HER polarization curve of Ag MDE in 10 mM trifluoromethanesulfonic acid (HOTf). HOTf instead of H2SO4 was used as the electrolyte for the MDE experiments since HOTf dissociates completely in water, which helps to simplify the GMPNP modeling. The onset potential for HER is −0.6 V vs SHE, and a current plateau is observed at −1.2 V vs SHE. As the potential sweeps to more negative than −1.8 V vs SHE, the current increases again. Through the comparison with the HER polarization curve measured in 10 mM potassium trifluoromethanesulfonate (KOTf, gray dashed curve), we can conclude that in 10 mM HOTf, the increase of current from ‒1.8 V vs SHE is originated from the reduction of water molecule, and H+ reduction is the predominant contribution to the current between ‒0.6 V and ‒1.8 V vs SHE. The plateau region of the curve from ‒1.2 V to −1.8 V vs SHE is due to the limitation of the mass transport of H+. As indicated by Fig. 3a, CO2 reduction on Ag NPs was mainly observed at the potential of this plateau region. Therefore, H+ reduction was the major competing reaction for CO2 reduction, and suppressing H+ reduction by retarding the mass transport of H+ is a possible strategy to increase the FE of CO2 reduction.
a HER polarization curves of Ag MDEs in 10 mM HOTf (solid curves): Bare Ag MDE (black), Ag MDEs covered by c-PDDA (orange), Sustainion XA-9 (blue), PTFE (dark yellow) and Nafion D520 (magenta). The gray and red dashed curves show the HER polarization curve of bare Ag MDE in 10 mM KOTf and 10 mM HOTf + 10 mM KOTf, respectively. The inset shows the enlargement in the pink region. b Comparison of the plateau current in the HER polarization curves. The averaged current from −1.2 V to −1.5 V vs SHE was taken as the plateau current. Source data are provided as a Source Data file.
Furthermore, Fig. 4a compares the HER polarization curves of Ag MDEs covered by c-PDDA, Sustainion XA-9, polytetrafluoroethylene (PTFE) and Nafion D520, respectively, in 10 mM HOTf, and that of bare Ag MDE in 10 mM HOTf + 10 mM KOTf. Figure 4b compares the plateau current of H+ reduction under different conditions. When the Ag MDE was covered by PTFE, a neutral polymer, the plateau was lower than that of bare Ag MDE, which can be ascribed to the lower diffusion coefficient of H+ in the polymer layer than in aqueous solution. Ag MDE covered by Nafion D520, a polymer bearing anionic sites45, showed higher plateau current than bare Ag MDE. Ag MDE covered by c-PDDA or Sustainion XA-9, polymers bearing cation sites, showed substantially lower plateau current than the Ag MDE covered by PTFE. Ag MDE covered by c-PDDA showed the lowest plateau current. These results indicate that the polymer layer bearing immobilized positive charge can suppress the mass transport of H+, and the higher the positive charge density is, the lower the mass transport rate of H+ is. It is noteworthy that the plateau current of bare Ag MDE in 10 mM HOTf + 10 mM KOTf is higher than that of cationic polymer decorated Ag MDE in 10 mM HOTf. Our previous study shows alkali cations can substantially suppress the migration rate of H+ but the diffusion of H+ cannot be significantly inhibited22. In metal cation-free solution, the migration rate of H+ equals the diffusion rate of H+ (see Supplementary Note 1 for the explanation). Therefore, once the migration of H+ is suppressed by the cationic polymer layer, the diffusion of H+ is suppressed simultaneously. As a consequence, the cationic polymer layer suppresses the mass transport of H+ more substantially than dissolved alkali cations.
GMPNP simulation was then conducted to understand how the cationic polymer layer suppresses the mass transport of H+. Figure 5a shows the model used for the simulation. Stern layer, the space between cathode and OHP, contains no charged species. A polymer layer is located outside the OHP with a charge density of the immobilized ionic sites of ρp. According to the loading of c-PDDA on Ag MDE in the experiments, the thickness of the polymer layer was set to 1 μm in the simulation. The polymer layer also contains movable H+, OH- and OTf- ions. Outside the polymer layer, H+, OH- and OTf- ions are the only charged species. The charge carried by the polymer layer modifies the electric field distribution according to Poisson equation:
a Model used for the simulation. The red curve illustrates the potential profile. ρ is the total charge density and ρp is the charge density carried by the polymer layer. b Migration rate of H+ with the electrode potential of −1.8 V vs SHE at 2 μm from OHP. Orange bars: Ag electrode covered by polymer layers with different ρp in 10 mM HOTf. Blue bar: Bare Ag electrode in 10 mM HOTf + 40 mM KOTf. c Potential profiles on Ag electrodes covered by polymer layers with different ρp (unit: C·cm−3) in 10 mM HOTf. The electrode potential is −1.8 V vs SHE. d Local pH at OHP of Ag electrodes at varied electrode potential. The solid curves represent Ag electrodes covered by polymer layers with different ρp (unit: C·cm-3) in 10 mM HOTf. The gray dashed curve represents bare Ag electrode in 10 mM HOTf + 40 mM KOTf. The horizontal red line indicates the bulk pH. Source data are provided as a Source Data file.
In this equation, φ is the potential, ρ is the total charge density of the immobilized ionic sites and movable ions, as shown in Fig. 5a, ε0 is the permittivity of vacuum and εr is the relative permittivity. Figure S20 shows the governing equations and boundary conditions used for the GMPNP simulation. Figure S21 shows the simulated polarization curves of H+ reduction with different ρp. The simulation reproduced the trend of the plateau current of H+ reduction in Fig. 4: The more positive ρp is, the lower plateau current is. Figure 5b shows the migration rate of H+ outside the polymer layer at −1.8 V vs SHE. At this potential, H+ reduction is limited by the mass transport of H+. The migration rate of H+ decreases when ρp increases, suggesting that cationic polymer layer can screen the electric field and suppress the migration of H+ while anionic polymer layer has the opposite effect. In addition, Fig. 5b shows that adding K+ ions into the acidic electrolyte can also suppress the migration of H+ on bare Ag electrode. In other word, both immobilized cations in the polymer layer and dissolved cations accumulated near the cathode can reduce the migration rate of H+, as illustrated in Fig. 1c, d. Moreover, Fig. 5c shows the simulated potential profiles with different ρp. When the polymer bears positive charge, the potential of the polymer layer is higher than the potential of bulk electrolyte, which is known as Donnan potential difference46,47. This layer with positive potential relative to bulk electrolyte acts as a barrier for the H+ mass transport from bulk electrolyte to the surface of cathode. The barrier becomes higher as ρp of the polymer layer increases. Figure S22 shows the profiles of electric field strength with different ρp. Strong electric field exists at the interface between charged polymer layer and solution due to the potential step at the interface. For Ag electrode covered by cationic polymer layer, the electric field is uniform within the polymer layer and solution. It is noteworthy that the electric field strength outside the polymer layer decreases as ρp increases, in accordance with the migration rate of H+ shown in Fig. 5b.
The charge of the polymer layer also affects the local pH near the cathode. Figure S23 shows the pH profiles with different ρp at −1.8 V vs SHE in 0.1 M HOTf. When the polymer layer is not charged, the pH at 10 nm to 1 μm from the OHP is higher than the bulk pH due to the concentration polarization. However, within 10 nm from the OHP, the pH is lower than the bulk pH since H+ ions are attracted electrostatically by the cathode. Figure 5d shows the pH at OHP at varied electrode potential. When ρp is negative or zero (magenta and black curves), the negative shift of the electrode potential does not drive the increase of pH at OHP. When the polymer layer bears positive charge, the pH value in the polymer layer increases drastically (Figure S23), and the local pH at OHP increases as the electrode potential shifts negatively beyond -0.9 V vs SHE (blue and orange curve in Fig. 5d). When ρp equals to +300 C·cm-3, the pH at OHP is higher than the bulk pH at the potential of the plateau region (<−1.2 V vs SHE). When K+ ions are contained in the acidic electrolyte and bare Ag electrode is used, pH at OHP increases as the electrode potential shifts negatively beyond −1.0 V vs SHE (gray dashed curve in Fig. 5d), in accordance with our previous reports9,22. Therefore, H+ reduction can drive local pH increase at OHP only when the cathode is covered by an immobilized cationic layer or the electrolyte contains inert cations. When CO2 reduction is involved, OH- anions generated from CO2 reduction can neutralize H+ and lead to further increase of local pH12. Therefore, the local pH under CO2 reduction condition should be higher than the value shown in Fig. 5d.
Besides retarding the migration of H+, the polymer layer also affects the electric field strength in Stern layer (denoted as EStern). The single-electron reduction of CO2 (CO2 + e- → CO2·-) is regarded as the rate determining step (RDS) of CO2 reduction to form CO in some reports48,49. As illustrated in Fig. 6a, the potential difference between the cathode and OHP is the driving force of the electron transfer from the cathode to CO2 molecules at OHP. It was also reported recently that chemisorption of CO2 on the catalytic site is the RDS50,51. The *CO2 species possesses the dipole moment towards the solution side and thus can be stabilized by the electric field in Stern layer. Therefore, no matter the reduction of CO2 follows which mechanism, it can be accelerated by the increase of EStern30,31,32,50.
a Potential profiles on Ag electrodes covered by polymer layers with ρp = 300 C·cm-3 (orange curve) and ρp = 0 (black curve) in 10 mM HOTf at −1.8 V vs SHE. Schematic of the rate determining step of CO2 reduction is shown. b Plots of the electric field strength in Stern layer based on the electrode potential. Solid curves: Ag electrodes covered by polymer layers with different ρp (unit: C·cm-3) in 10 mM HOTf. Gray dashed curve: Bare Ag electrode in 10 mM HOTf + 40 mM KOTf. Source data are provided as a Source Data file.
The value EStern was extracted from the result of GMPNP simulations. As shown in Fig. 6a, the black and the orange curves are the potential profiles on Ag electrode covered by polymer layers with ρp of 0 and +300 C cm-3 at −1.8 V vs SHE, respectively. When ρp equals to +300 C cm-3, EStern (the slope of the curve in Stern layer) is higher, suggesting that the cationic polymer layer can promote CO2 reduction on Ag electrode. Figure 5b compares the values of EStern on Ag electrode covered by polymer layer with different ρp at varied electrode potential. For Ag electrodes covered by neutral or anionic polymer layer (ρp ≤ 0, black and magenta curves), EStern first increases and then keeps constant as the electrode potential shifts negatively. Consequently, when the potential is more negative than −1.1 V vs SHE, CO2 reduction cannot be accelerated by applying larger overpotential. For Ag electrode covered by cationic polymer layer (ρp > 0, blue and orange curves), EStern increases continuously as the electrode potential shifts negatively. Moreover, EStern is higher when ρp is more positive. The dashed gray curve in Fig. 6b plots EStern on bare Ag electrode in K+-containing acidic electrolyte. The promotion effect on EStern induced by the polymer layer with ρp of 300 C·cm-3 is comparable to the effect induced by the addition of K+ at −1.2 V to −1.9 V vs SHE. Considering that CO2 reduction occurs on Ag catalyst in this potential range (Fig. 3a), a cationic polyelectrolyte with ρp = 300 C·cm-3 and K+ ions should show comparable promoting effect on CO2 reduction.
We also simulated how the thickness of the polymer layer affects the migration of H+ and the value of EStern. As shown in Figure S24, the rate of H+ migration decreases as the thickness of the polymer layer increases, while the thickness of the polymer layer shows negligible effect on the value of EStern. Therefore, H+ reduction can be suppressed by increasing ρp or increasing the thickness of the polymer layer, but CO2 reduction can be promoted only by increasing ρp of the polymer layer. If the polymer layer can be compressed under the electrostatic attraction generated from the cathode, ρp at the cathode side should increase. As shown in Figure S25, the accumulation of cationic site to the cathode side leads to lower migration rate of H+ and higher EStern. Both effects result in improved selectivity of CO2 reduction.
In summary, by decorating catalysts with c-PDDA, a cross-linked polyelectrolyte with high cation density, CO2 reduction in metal cation-free acidic electrolyte was realized. CO and formic acid were produced with high Faradaic efficiency on Ag and In catalysts, respectively. Electrochemical measurements with MDE and GMPNP simulations indicate that the cationic sites carried by the polymer layer play a similar role as alkali cations dissolved in acidic electrolyte on enabling CO2 reduction, namely, suppressing the migration of H+ and enhancing the electric field in Stern layer. Conducting CO2 reduction in metal cation-free acidic electrolyte helps to improve the sustainability of CO2 reduction technique by maintaining the pH of electrolyte and inhibiting the flooding through GDE.
For the preparation of materials, Ag powder (99.99%, <100 nm, Macklin), InCl3 (99.9%, Bide), NaBH4 (98%, Aladdin), tetraethylene glycol (TEG, 99%, Aladdin), DADMACl (60% aqueous solution, Macklin), DAMA (99.5%, Bide), Ethylenediaminetetraacetic acid disodium salt (Na2EDTA, 98%, Bide), (NH4)2S2O8 (99.99%, Macklin), NaOH (99%, Macklin), 1,6-diiodohexane (98%, Bide), ethylene glycol (99.5%, Xilong), Nafion D520 (5% in a mixture of lower aliphatic alcohols and water, DuPont), Sustainion XA-9 (alkaline ionomer 5% in ethanol, Dioxide Material) and PTFE (60 wt.% in water, 9dingchem) were used without further purification. For the preparation of electrolyte, H2SO4 (98%, ultrapure for trace metal analysis, Aladdin), K2SO4 (99.99%, Aladdin), HOTf (99%, Energy Chemical) and KOH (99.999%, Aladdin) were used. Pre-electrolysis (constant current electrolysis at −20 mA for 1 hour) was conducted for the HOTf solution before usage. Ultrapure water (18.2 MΩ cm) was used for all experiments.
0.20 g of InCl3 was dissolved in 30 mL of deionized water. 0.14 g of NaBH4 was dissolved in 10 mL of TEG. The solution of NaBH4 was dropped into the solution of InCl3 under stirring and the mixture was further stirred at 25 °C for 2 h. In NPs were then separated by centrifugation and washed by ethanol for 3 times. Finally, In NPs were dried under vacuum at 60 °C for 12 hours.
First, 6.9 mL of the aqueous solution of DADMACl (60 wt.%), 1.1 mL of DAMA and 0.20 mL of condensed H2SO4 were mixed to form a uniform solution. Next, 20 mg of (NH4)2S2O8 and 20 mg of Na2EDTA were added into this solution. This solution was stirred at 60 °C in Ar atmosphere for 4 hours. Then, 0.3 g of NaOH was added to neutralize the solution. White precipitate was then formed by adding 10 mL of acetone. The precipitate was separated by filtration and washed by ethanol for 3 times. Finally, the precipitate was dried under vacuum to give the copolymer of DADMACl and DAMA.
First, 0.5 mL aqueous solution containing 2.6 mg of the copolymer of DADMACl and DAMA, 10 mg of the catalyst powder (Ag NPs or In NPs) and 0.5 mL of ethylene glycol were mixed and sonicated to form a uniform ink. Then, 20 μL of 1,6-diiodohexane was dissolved into 0.5 mL of ethanol and this solution was added into the ink and sonicated. The ink was loaded onto the GDE (Sigracet 29BC, 1×2 cm2) on a heat plate at 170 °C with drop-casting method. The loading of the catalyst was 5 mg·cm-2. The solvent was evaporated after 30 minutes. The electrode was then immersed in 10 mL of ethanol solution containing 40 μL of 1,6-diiodohexane and heat at 70 °C for 12 hours. Finally, the electrode was rinsed with ethanol and dried under vacuum.
To prepare the ink of PDDA decorated catalyst, 1 mL of aqueous solution containing 3 mg of PDDA, 1 mL of ethanol and 10 mg of catalyst was mixed. To prepare the ink of Sustainion XA-9 decorated catalyst, 1 mL of ethanol solution containing 3 mg of Sustainion XA-9, 1 mL of deionized water and 10 mg of catalyst was mixed. The ink was sonicated for 1 hour and dropped onto the GDE (1 × 2 cm2) on a heat plate at 120 °C. The loading of the catalyst was 5 mg cm-2.
Polycrystalline Ag MDE with the diameter of 25 μm was used. The MDE is embedded in a glass mantle with the diameter of 4 mm. To prepare Ag MDE covered by c-PDDA, the aqueous solution of the copolymer of DADMACl and DAMA was dilute to 3 mg mL-1, and 2 μL of this solution was dropped onto the Ag MDE to cover the Ag surface and the mantle. The MDE was dried under infrared irradiation. Then, 40 μL of 1,6-diiodohexane was dissolved in 10 mL of ethanol, and the MDE was immersed in this solution at 70 °C for 12 h. Finally, the MDE was rinsed with ethanol and dried for further electrochemical measurement. To prepare Ag MDE covered by Nafion D520, Sustainion XA-9 or PTFE, the polymer dispersion was diluted by ethanol to 3 mg mL-1, and 2 μL of this solution was dropped onto the Ag MDE to cover the Ag surface and the mantle. The MDE was dried for further electrochemical measurement.
The XPS characterizations were performed on an ULVAC-PHI 5000 VersaProbe III XPS system using monochromatic Al Kα radiation (1486.6 eV). HAADF-STEM and EDS mapping images were collected on an FEI Tecnai F30 operated at 300 kV. XRD patterns were collected on a Rigaku SmartLab X-ray powder diffractometer with Cu Kα radiation (λ = 1.5406 Å, 45 kV, and 200 mA). SEM characterizations were performed on ZEISS Merlin SEM with the EDAX Octane Pro energy dispersive X-ray spectroscopy system. ICP-MS measurements were conducted on Agilent 7700X ICP-MS. 1H-nuclear magnetic resonance (1H-NMR) spectra were measured on AVANCE III 400 MHz. Element analysis was conducted on Elementar Vario EL cube. Molecular weight distribution of the copolymer was measured by Agilent gel permeation chromatography (GPC) 50 with water as the mobile phase.
A glass slide with known mass, thickness and area was used as a substrate. The layer of c-PDDA was deposited onto this glass slide with the same method of the preparation of the working electrode, except that the glass slide was used instead of the GDE and the catalyst was not added. Then, the mass and thickness of the slide after polymer deposition were measured to obtain the volume and the mass of the c-PDDA layer in dry form. Next, the slide was immersed in water for 30 minutes. The four sides of this slide were blocked by other glass slides to prevent the film of c-PDDA from swelling out of the slide. Then, the average thickness of the slide was measured by screw caliper to calculate the volume of the c-PDDA layer in wet form. The weight content of nitrogen in the dry form of c-PDDA was also measured through element analysis. The XPS spectrum (Figure S1d) indicates all N element in c-PDDA was in quaternary ammonium form. Thus, the cation density (unit: mmol·g-1) of the dry form of c-PDDA was calculated. From the mass and cation density of the dry form and the volume of the wet form, we calculated the charge density (unit: C·cm-3) of the wet form of c-PDDA.
All electrochemical experiments were conducted at 25 °C on an IVIUM potentiostat (Vertex.20 V.EIS). A three-chamber flow cell was used as the electrolyzer. The GDE as the working electrode and a Ag/AgCl/saturated KCl electrode as the reference electrode were in one chamber. All potential values were converted to SHE scale according to: φ(vs SHE) = φ(vs Ag/AgCl/saturated KCl) + 0.197 V. An IrO2-decorated Ti foil as the counter electrode was in the other chamber. These two chambers were separated by a Nafion-211 membrane. 0.1 M H2SO4 was used as the flowing electrolyte. The catholyte and the anolyte were circulated separately by two peristaltic pumps. The volumes of catholyte and anolyte were both 30 mL and the flow rates were both 10 mL·min-1. CO2 was fed through a gas chamber behind the GDE. The flow rate was fixed at 30 standard cubic centimeter per minute (sccm) by a mass flow controller. Electrolysis was conducted with chronopotentiometry method. Resistance of the electrolyte was measured by impedance spectroscopy at −1.0 V vs SHE for all electrolytes (Table S1), and the real electrode potential (φreal) was manually calculated with full iR compensation after electrolysis according to φreal = φmeasured – iR. The average Averaged potentials were then reported. The gas phase products (H2 and CO) were quantified by an online gas chromatography (GC9790Plus, FULI INSTRUMENTS). The FEs of gas phase products were calculated based on the flow rate of the outlet gas from the flow cell measured by a soap film flowmeter. The liquid phase product (formic acid) was quantified by 1H-NMR with dimethyl sulfoxide (DMSO) as the inner standard. The pH values of catholyte and anolyte were measured by a pH meter. To measure the mass of electrolyte permeating through the GDE, a piece of filtrate paper and a piece of cotton wool were put behind the GDE (in the gas chamber) to absorb the solution passing through the GDE, and the change of the total mass of the filtrate paper and the cotton wool before and after electrolysis was weighed. The measurements of mass of electrolyte permeating the GDE (Fig. 2d) and the CO2 reduction performances of c-PDDA decorated Ag NPs and In NPs (FEs and electrode potentials shown in Fig. 3a, b) were replicated with three electrodes prepared separately, respectively. The standard deviations were then calculated.
A Ag/AgCl/saturated KCl electrode was used as the reference electrode. At Pt wire was used as the counter electrode. The measurement was conducted in a single-chamber cell. 10 mM HOTf solution was used as the electrolyte. HER polarization curves were collected with linear sweep voltammetry (LSV) method with the sweeping rate of 100 mV s-1. The iR compensation was not conducted due to the small current.
GMPNP modeling was conducted to simulate H+ reduction reaction in HOTf solution on Ag electrode covered by immobilized layer of polyelectrolyte. Figure S20 shows the geometry, governing equation and boundary conditions used for the simulation. Steady-state simulation was conducted. The conservation of mass gives:
In this equation, Ji is the flux of species i (i = H+, OTf- and OH-). Ri is the rate of homogeneous reaction in which species i is involved. OTf- does not participate in any homogeneous reaction, while H+ and OH− are involved in neutralization reaction and dissociation of water. Ji is expressed as:
In this equation, Di, Ci and zi are the diffusion coefficient, concentration, and charge of species i, respectively. φ is the potential, F is the Faradaic constant, R is the gas constant, T is the temperature (298 K). γi is the ‘Langmuir type’ activity coefficient. The first and second terms on the right side of Eq. 3 correspond to the diffusion rate and the migration rate. The Poisson equation (Eq. (1)) and the conservations of mass (Eq. (2)) were solved simultaneously by COMSOL (v.6.0) with a MUMPS solver with a nonlinear automatic Newton method. Detailed procedures are in the ‘Simulation section’ of Supplementary Information. All parameters and coefficients used in the simulation are listed in Table S2. Considering that the values of Di are affected by the structure of polymer and the value of εr varies according to the local environment, GMPNP simulations with different values of Di and εr were also conducted to check whether the variation of these parameters affects the conclusion of the simulation. The results are summarized in Supplementary Note 2 (GMPNP simulations with varied diffusion coefficients and relative permittivity) and Tables S3-5.
Source data are provided in this paper. More data that support the findings of this study can be found in the Supplementary Information. Raw data are also available from the corresponding author upon request. Source data are provided in this paper.
Seh, Z. W. et al. Combining theory and experiment in electrocatalysis: Insights into materials design. Science 355, eaad4998, (2017).
Lees, E. W., Mowbray, B. A. W., Parlane, F. G. L. & Berlinguette, C. P. Gas diffusion electrodes and membranes for CO2 reduction electrolysers. Nat. Rev. Mater. 7, 55–64 (2022).
Article ADS CAS Google Scholar
Rabinowitz, J. A. & Kanan, M. W. The future of low-temperature carbon dioxide electrolysis depends on solving one basic problem. Nat. Commun. 11, 5231 (2020).
Article ADS CAS PubMed PubMed Central Google Scholar
Zhang, B. A., Ozel, T., Elias, J. S., Costentin, C. & Nocera, D. G. Interplay of homogeneous reactions, mass transport, and kinetics in determining selectivity of the reduction of CO2 on Gold Electrodes. ACS Cent. Sci. 5, 1097–1105 (2019).
Article CAS PubMed PubMed Central Google Scholar
Chen, C., Li, Y. & Yang, P. Address the “alkalinity problem” in CO2 electrolysis with catalyst design and translation. Joule 5, 737–742 (2021).
Ozden, A. et al. Cascade CO2 electroreduction enables efficient carbonate-free production of ethylene. Joule 5, 706–719 (2021).
Ma, M. et al. Insights into the carbon balance for CO2 electroreduction on Cu using gas diffusion electrode reactor designs. Energy Environ. Sci. 13, 977–985 (2020).
O’Brien, C. P. et al. Single Pass CO2 Conversion Exceeding 85% in the Electrosynthesis of Multicarbon Products via Local CO2 Regeneration. ACS Energy Lett. 6, 2952–2959 (2021).
Gu, J. et al. Modulating electric field distribution by alkali cations for CO2 electroreduction in strongly acidic medium. Nat. Catal. 5, 268–276 (2022).
Wang, Z., Hou, P., Wang, Y., Xiang, X. & Kang, P. Acidic electrochemical reduction of CO2 using nickel nitride on multiwalled carbon nanotube as selective catalyst. ACS Sustain. Chem. Eng. 7, 6106–6112 (2019).
Wu, Y. et al. Electrochemical CO2 reduction using gas diffusion electrode loading Ni-doped covalent triazine frameworks in acidic electrolytes. Electrochemistry 88, 359–364 (2020).
Bondue, C. J., Graf, M., Goyal, A. & Koper, M. T. M. Suppression of hydrogen evolution in acidic electrolytes by electrochemical CO2 reduction. J. Am. Chem. Soc. 143, 279–285 (2021).
Article CAS PubMed Google Scholar
Huang, J. E. et al. CO2 electrolysis to multicarbon products in strong acid. Science 372, 1074–1078 (2021).
Article ADS CAS PubMed Google Scholar
Monteiro, M. C. O., Philips, M. F., Schouten, K. J. P. & Koper, M. T. M. Efficiency and selectivity of CO2 reduction to CO on gold gas diffusion electrodes in acidic media. Nat. Commun. 12, 4943 (2021).
Article ADS CAS PubMed PubMed Central Google Scholar
Xie, Y. et al. High carbon utilization in CO2 reduction to multi-carbon products in acidic media. Nat. Catal. 5, 564–570 (2022).
Ma, Z. et al. CO2 electroreduction to multicarbon products in strongly acidic electrolyte via synergistically modulating the local microenvironment. Nat. Commun. 13, 7596 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Pan, B. et al. Close to 90% single-pass conversion efficiency for CO2 electroreduction in an acid-fed membrane electrode assembly. ACS Energy Lett. 7, 4224–4231 (2022).
Qiao, Y. et al. Engineering the local microenvironment over Bi nanosheets for highly selective electrocatalytic conversion of CO2 to HCOOH in strong acid. ACS Catal. 12, 2357–2364 (2022).
Zhao, Y. et al. Conversion of CO2 to multicarbon products in strong acid by controlling the catalyst microenvironment. Nat. Synth. (2023).
Li, H. et al. Tailoring acidic microenvironments for carbon-efficient CO2 electrolysis over Ni-N-C catalyst in a membrane electrode assembly electrolyzer. Energy Environ. Sci. (2023).
Nie, W., Heim, G. P., Watkins, N. B., Agapie, T. & Peters, J. C. Organic additive-derived films on Cu electrodes promote electrochemical CO2 reduction to C2+ products under strongly acidic conditions. Angew. Chem. Int. Ed. 62, e202216102 (2023).
Qin, H.-G. et al. Quantitative understanding of cation effects on the electrochemical reduction of CO2 and H+ in acidic solution. ACS Catal. 13, 916–926 (2023).
Moss, A. B. et al. In operando investigations of oscillatory water and carbonate effects in MEA-based CO2 electrolysis devices. Joule 7, 350–365 (2023).
Bui, J. C. et al. Engineering catalyst–electrolyte microenvironments to optimize the activity and selectivity for the electrochemical reduction of CO2 on Cu and Ag. Acc. Chem. Res. 55, 484–494 (2022).
Article CAS PubMed Google Scholar
Verma, S. et al. Insights into the low overpotential electroreduction of CO2 to CO on a supported gold catalyst in an alkaline flow electrolyzer. ACS Energy Lett. 3, 193–198 (2018).
Article ADS CAS Google Scholar
Cofell, E. R., Nwabara, U. O., Bhargava, S. S., Henckel, D. E. & Kenis, P. J. A. Investigation of electrolyte-dependent carbonate formation on gas diffusion electrodes for CO2 electrolysis. ACS Appl. Mater. Interfaces 13, 15132–15142 (2021).
Article CAS PubMed Google Scholar
Leonard, M. E., Clarke, L. E., Forner-Cuenca, A., Brown, S. M. & Brushett, F. R. Investigating electrode flooding in a flowing electrolyte, gas-fed carbon dioxide electrolyzer. ChemSusChem 13, 400–411 (2020).
Article CAS PubMed Google Scholar
Monteiro, M. C. O., Dattila, F., López, N. & Koper, M. T. M. The role of cation acidity on the competition between hydrogen evolution and CO2 reduction on gold electrodes. J. Am. Chem. Soc. 144, 1589–1602 (2022).
Article CAS PubMed Google Scholar
Monteiro, M. C. O. et al. Absence of CO2 electroreduction on copper, gold and silver electrodes without metal cations in solution. Nat. Catal. 4, 654–662 (2021).
Chen , LD , Urushihara , M. , Chan , K. & Nørskov , JK Electric field effects in electrochemical CO2 reduction . ACS Catalog. 6, 7133–7139 (2016).
Resasco, J. et al. Promoter effects of alkali metal cations on the electrochemical reduction of carbon dioxide. J. Am. Chem. Soc. 139, 11277–11287 (2017).
Article CAS PubMed Google Scholar
Ringe, S. et al. Understanding cation effects in electrochemical CO2 reduction. Energy Environ. Sci. 12, 3001–3014 (2019).
Shin, S.-J. et al. A unifying mechanism for cation effect modulating C1 and C2 productions from CO2 electroreduction. Nat. Commun. 13, 5482 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Kutz, R. B. et al. Sustainion imidazolium-functionalized polymers for carbon dioxide electrolysis. Energy Technol. 5, 929–936 (2017).
Liu, M.-N., Chen, W.-G., Liu, H.-J. & Chen, Y. Facile synthesis of intrinsically photoluminescent hyperbranched polyethylenimine and its specific detection for copper ion. Polymer 172, 110–116 (2019).
Marquardt, F., Bruns, M., Keul, H., Yagci, Y. & Möller, M. Light-induced cross-linking and post-cross-linking modification of polyglycidol. Chem. Commun. 54, 1647–1650 (2018).
Yang, L.-F., Qin, H.-G., Li, F.-Z., Peng, J.-Z. & Gu, J. Cation modified Fe–N–C catalyst for the electrochemical reduction of nitrate in solutions of low ionic strength. Inorg. Chem. Front. 10, 942–951 (2023).
Haynes, W. M., Lide, D. R. & Bruno, T. J. CRC Handbook of Chemistry and Physics. 97th. edn, (CRC Press, 2016).
Li, W. et al. Bifunctional ionomers for efficient co-electrolysis of CO2 and pure water towards ethylene production at industrial-scale current densities. Nat. Energy 7, 835–843 (2022).
Article ADS CAS Google Scholar
Gao, Z. et al. Promoting electrocatalytic CO2 reduction via anchoring quaternary piperidinium cations onto copper electrode. Electrochim. Acta 458, 142509 (2023).
Koshy, D. M. et al. Chemical modifications of Ag catalyst surfaces with imidazolium ionomers modulate H2 evolution rates during electrochemical CO2 reduction. J. Am. Chem. Soc. 143, 14712–14725 (2021).
Article CAS PubMed Google Scholar
Kim, C. et al. Tailored catalyst microenvironments for CO2 electroreduction to multicarbon products on copper using bilayer ionomer coatings. Nat. Energy 6, 1026–1034 (2021).
Article ADS CAS Google Scholar
Wang, H., Thiele, A. & Pilon, L. Simulations of cyclic voltammetry for electric double layers in asymmetric electrolytes: a generalized modified Poisson–Nernst–Planck model. J. Phys. Chem. C 117, 18286–18297 (2013).
Bohra, D., Chaudhry, J. H., Burdyny, T., Pidko, E. A. & Smith, W. A. Modeling the electrical double layer to understand the reaction environment in a CO2 electrocatalytic system. Energy Environ. Sci. 12, 3380–3389 (2019).
Mauritz, K. A. & Moore, R. B. State of understanding of Nafion. Chem. Rev. 104, 4535–4586 (2004).
Article CAS PubMed Google Scholar
Donnan, F. G. The theory of membrane equilibria. Chem. Rev. 1, 73–90 (1924).
Kamcev, J., Paul, D. R. & Freeman, B. D. Effect of fixed charge group concentration on equilibrium ion sorption in ion exchange membranes. J. Mater. Chem. A 5, 4638–4650 (2017).
Wuttig, A., Yaguchi, M., Motobayashi, K., Osawa, M. & Surendranath, Y. Inhibited proton transfer enhances Au-catalyzed CO2-to-fuels selectivity. Proc. Natl Acad. Sci. USA 113, E4585–E4593 (2016).
Article ADS CAS PubMed PubMed Central Google Scholar
Zhu, X., Huang, J. & Eikerling, M. Electrochemical CO2 reduction at silver from a local perspective. ACS Catal. 11, 14521–14532 (2021).
Ringe, S. et al. Double layer charging driven carbon dioxide adsorption limits the rate of electrochemical carbon dioxide reduction on Gold. Nat. Commun. 11, 33 (2020).
Article ADS CAS PubMed PubMed Central Google Scholar
Vijay, S. et al. Unified mechanistic understanding of CO2 reduction to CO on transition metal and single atom catalysts. Nat. Catal. 4, 1024–1031 (2021).
This work was supported by the National Natural Science Foundation of China (no. 22272073 to J.G.), Shenzhen Science and Technology Program (no. JCYJ20210324104414039, no. JCYJ20220818100410023 and no. KCXST20221021111207017 to J. G.), Guangdong Grants (2021ZT09C064 to J.G.), Guangdong Basic and Applied Basic Research Foundation (no. 2021A1515110360 and no. 2022A1515011976 to J.G.) and the “Climbing Program” Special Funds (no. pdjh2023c10301 to Y.-Y.B.).
Department of Chemistry, Southern University of Science and Technology, Shenzhen, Guangdong, China
Hai-Gang Qin, Yun-Fan Du, Yi-Yang Bai, Fu-Zhi Li, Xian Yue, Hao Wang, Jian-Zhao Peng & Jun Gu
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
J.G. supervised this research project. H.-G.Q. conducted electrochemical measurements and simulations. Y.-F.D. and J.-Z.P. synthesized the copolymer. Y.-Y.B. conducted the MDE experiments. F.-Z.L. and X.Y. conducted sample characterization. H.-G.Q. and H.W. synthesized the catalysts. H.-G.Q. and J.G. wrote the manuscript.
Chinese patent application (no. 2023107001339) was filed by the Southern University of Science and Technology with J. G., H.-G.Q., and Y.-F.D. as inventors. This patent pertains to the synthesis of c-PDDA and the uses of c-PDDA decorated Ag and In nanoparticles for electrocatalytic applications. Y.-Y.B., F.-Z.L., X.Y., H.W., and J.-Z.P. declare no competing interests.
Nature Communications thanks Remco Hartkamp, Ngoc Huan Tran, and the other anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
Qin, HG., Du, YF., Bai, YY. et al. Surface-immobilized cross-linked cationic polyelectrolyte enables CO2 reduction with metal cation-free acidic electrolyte. Nat Commun 14, 5640 (2023). https://doi.org/10.1038/s41467-023-41396-2
DOI: https://doi.org/10.1038/s41467-023-41396-2
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
Nature Communications (Nat Commun) ISSN 2041-1723 (online)
Water Soluble Fertiliser Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.